Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

    • Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material
    • Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material
    • Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material
  • Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

    Product Details:

    Place of Origin: CHINA
    Brand Name: MK
    Model Number: MCO-W

    Payment & Shipping Terms:

    Minimum Order Quantity: 20000 sheets or 2 tons
    Price: Negotiable
    Packaging Details: by reel or 500 sheets per bag / 4-8 bags per paper carton , or as per customer requirements . All the cartons are firmly piled up and fixed on the solid plywood pallet
    Delivery Time: 7-15 working days
    Payment Terms: D/A, D/P, T/T, Western Union, L/C
    Supply Ability: 5000K per week
    Contact Now
    Detailed Product Description
    Normal Thickness: 0.04,0.05,0.06,0.08,0.10mm Vicat Softening Point: About 72±2 ℃
    Tensile Strength: ≥40 MPa Heating Shrinkage Ratio: ≤10%
    Aging Time: >200 Hours Storage Condition: Sealed, Moisture-proof, Room Temperature Under 40℃

    Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

     

    1. Features of Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

    PVC Coated Overlay MCO-W model is suitable for laminating with most PVC sheets printed by various printers. It features high adhesion, no color change and deformation.
    It is applicable to almost all sheets printed by various ink. It features excellent peeling strength and long aging time.

    Technical Parameters:

    Item Parameters
    Vicat softening point    72±2 ℃
    Heating Shrinkage ratio    ≤10 %
    Tensile Strength ≥40 MPa
    Normal thickness in mm 0.04,0.05,0.06,0.08,0.10
    Peel Strength (90°, 300mm/min) ≥6.0 N/cm
    Aging time (65℃ temp./95% humidity ) >200 hours
     Suitable ink offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink

    Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

    2.Characters of Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

       ●    Suitable for lamination with Inkjet printer Ink, with excellent peel strength.

     ● Abrasion resistant , prolong the life of cards.

     ● Environment friendly in the card making process, no solvent or gas discharges.

    Item Parameters
    Surface Clean and flatness
    Dimensional Tolerance (mm) ±1
    Angle Cut Tolerance (mm) ±1
    Diagonal Difference (mm) ≤1
    Thickness Tolerance (mm) ±10%
    Vicat (℃) 72±2
    Shrinkage MD ≥ - 40%
    TD ≤15%
    Tensile Strength (MPa) MD ≥35
    TD ≥35

    Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

     

    Product name Thickness Range  Color Vicat ℃ dynes/cm Apparent density g/cm3 Peel strength N/cm Main application
    PVC coated overlay 0.04~0.10mm Transparent 72-76 34~44 1.12~1.30 / It is mainly used for various magnetic stripe cards, phone cards, membership cards and other PVC cards, adhesive force is more than 3.5N. .

     

    3. Laminating condition of Lamination PVC Coated Overlay Film With Strong Adhension For Smart Card Material

    Laminating Unit Temp(℃) Pressure(MPa) Time (min)
    Heat Laminating 110~130 ≥8 20
    Cool Laminating ≤20 ≥8 20
     